The mechanical performance change of 1060 industry pure aluminum which had been processed under room temperature condition using accumulative rollbonding(ARB) was analyzed.The experimental results indicate that the material tensile strength and microhardness were enhanced with rolling pass increase.The dimple of the fracture gradually became smaller and shallower but it was still gliding fracture.The elongation percentage dropped remarkably at the first pass,and then its changes was smooth with the rolling pass increase.After five cycles,the material obtained fairly good mechanical properties.Compared to the properties of the parent metal,the tensile strength enhanced to 210 MPa approximately 2.41 times,the microhardness enhanced to 78.5 HV about 2.2 times and the elongation percentage was 9.3% only 0.21 times.
引用该论文:Lv Shuang,WANG Kuai-she,ZHANG Bing,YIN Juan. Mechanical Properties of ARB 1060 Industry Pure Aluminum[J]. Materials for mechancial engineering, 2008, 32(3): 75~77 糖心产精国品免费入口*完整版,糖心产精国品免费入口*完整版,糖心产精国品免费入口*完整版,糖心产精国品免费入口*完整版. 1060工业纯铝累积叠轧后的糖心产精国品免费入口*完整版[J]. 机械工程材料, 2008, 32(3): 75~77
论文评价
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
分享论文
参考文献
【1】Tsuji N,Okuno S,Matsuura T,et al.Mechanical properties as a function of grain size in ultrafine grained aluminum and iron fabricated by ARB and annealing process[J].Materials Science Forum,2003,426/432(3):2667-2672.
【2】Reis Ana,Carmen C,Kestens Leo.Cross-sectional texture gradients in interstitial free steels processed by accumulated roll bonding[J].Solid State Phenomena,2005,105:233-238.
【3】Lee Seong-Hee,Utsunomiya Hiroshi,Sakai Tetsuo.Microstructures and mechanical properties of ultra low carbon interstitial free steel severely deformed by a multi-stack accumulative roll bonding process[J].Materials Transactions,2004,45(7):2177-2181.
【4】Kaneko S,Fukuda K,Utsunomiya H,et al.Ultra grain refinement of aluminium 1100 by ARB with cross rolling[J].Materials Science Forum,2003,432(3):2649-2654.
【5】Hoppel Heinz Werner,May Johannes,Goken Mathias.Enhanced strength and ductility in ultrafine-grained aluminium produced by accumulative roll bonding[J].Advanced Engineering Materials,2004,6(4):219-222.
【9】Saito Y,Utsunomiya H,Tsuji N,et al.Novel ultra-high straining process for bulk materials development of the accumulative roll-bonding process[J].Acta Mater,1999,47(2):579-583.